TIN

TECHNICAL FEATURES

Found as bars and ingots. Bar lengths are 70-80cm.

PHYSICAL FEATURES

COMPOSITION %

99.8 (min)

SPECIFIC WEIGHT (Kg/dm³)

7,31

FUSION TEMPERATURE (˚C)

232

HEAT CONDUCTIVITY AT 25˚C AS ANNEALED (Kcal/Hr/Cm/˚C)

55

COEFFICIENT OF EXPANSION (20-200 ˚C)(˚C) X 10-6

23.Nis

HEATING TEMPERATURE (20 ˚C),(Kcal/Kg/˚C)

0.054

SPECIFIC RESISTANCE (20˚C tavlanmış)(μΩ-cm)

11,5

MECHANIC FEATURES

ELASTIC MODULE IN STRESS (Kg/cm²)x10³

420-455

TENSILE STRENGTH AT 24˚C (Kg/cm²)

195

YIELDING STRENGTH AT 24˚C (Kg/cm²)

140

STRETCHING 24˚C (5 cm) %

35

HARDNESS

8

LIMIT OF IMPACT RESISTANCE (IZOD) (KG-M/M)

1,93

STRENGTH LIMIT (Kg/cm²)

240

PROCESSING FEAUTRES

CASTING TEMPERATURE (KOKİL),(˚C)

275-290

WELDING FEATURES

With a simple fusion, two parts can be combined. Large and heavy parts such as blocks and pipes can be welded using eutectic and tin-lead solder or melting alloys with low fusion points.

CORROSION FEATURES

Resistant to distilled, salty and fresh water. Affected by strong acids, alkalis and acid salts. Oxygen presence in solution increases response speed.

AVAILABILITY

Ingot, rod, wire, foil

AREAS OF USE

Packaging industry, electric and electronic industry, coating (Tinning), alloying